Physical Properties of Nimonic 80A Alloy Wire

The nimonic 80A is a age hardenable nickel chromium allow wire, high strength due to presence of titanium, aluminum and carbon made for service at different temperatures about 815oC or 1500ooF. It is made by high frequency melting and casting in the presence of air for extruded forms. The electroslag refined alloy material is utilized for forging.

The nimonic 80A wire is employed in making the gas turbine components like blades, rings and discs, bolts, nuclear boiler tube parts, die casting and automobile’s valves. The chemical composition of nimonic 80A is mentioned here below:

Carbon 0.10
Chromium 18.0-21.0
Silicon 1.0
Copper 0.2
Iron 3.0
Manganese 1.0
Titanium 1.8-2.7
Aluminum 1.0-1.8
Cobalt 2.0
Boron 0.008
Zirconium 0.15
Lead 0.0025
Sulfur 0.015
Nickel Bal.

The physical properties of nimonic 80A are provided in the below table:

Density, g/cm3 8.19
Melting Range, oC or oF 1320-1365 or 2410-2490
Mass Susceptibility 5.85 x 10-6 at 1000 gauss
Volume Susceptibility 4.78 x 10-5 at 1000 gauss
Magnetic Permeability 1.000601 for 200-2000 oersted

The density of alloy is concluded on the extruded bar, immediately formed and extruded part, immediately cold drawn at the heat processing of 8 hours at temperature of 1080oC or 1976oF then air quenched plus heat processing for 6 hours at temperature of 700oC or 1292oF the air quenched. The liquefaction temperature is calculated by the inverse cooling method and the solidification by the metallographic tests. The accuracy is concluded by ±5oC or 9oF for liquefaction and +0 at -10oC or 18oF for the solidification.

The specific heat properties of alloy are provided in the below table:

oC oF J/kg oC Btu/lb oF
20 68 448 0.107
100 212 469 0.112
200 392 494 0.118
300 572 519 0.124
400 752 548 0.131

The thermal conductivity of alloy is shown in the below table:

oC oF W/m •°C Btu/ft•h•°F
20 68 11.2 6.47
100 212 11.6 6.71
200 392 14.4 8.32
300 572 16.1 9.31
400 752 17.8 10.3

The alloy is cold drawn sheet, heat processed for 2 to 3 minutes at 1150oC or 2102oF  then fluidized bed cooled and heating for 1 hour at 925oC or 1697oF, air quenched and heating for 4 hours at 750oC or 1382oF then air cooled. The mean coefficient of thermal expansion properties of alloy are shown below:

oF 10-6/oF
A B
68 – 212 7.1 7.1
– 392 7.4 7.4
– 572 7.6 7.6
– 752 7.8 7.8
– 932 8.0 8.1
–1112 8.3 8.3

The creep resistance offered by the nimonic 80A is analyzed. The total plastic strain information is calculated on the extruded bar. The creep resistance on the extruded bar, then forged is calculated by following the Larson-Miller presentations and Graham and Walles techniques.

According to Graham and Walles method the stresstime test aspects meet on the continuous array of straight line at the different temperatures.  the total plastic strain for the extruded section then cold drawn and cold rolled sheet are described in the below table:

oC and oF Strain% Stress, MPa (ksi), to give total plastic strain in:
100h 300h 1000h 3000h 10,000h 30,000h
600, 1112 0.1 558 (80.9) 511 (74.1) 460 (66.7) 412 (59.7) 371 (53.8)
650, 1202 0.1 454 (65.8) 403 (58.4) 347 (50.3) 298 (43.2)
700. 1292 0.1 346 (50.2 295 (42.8) 238 (34.5) 190 (27.6) 147 (21.3)
750, 1382 0.1 239 (34.7) 192 (27.8) 144 (20.9) 108 (15.7) 74 (10.7)*
815, 1499 0.1 124 (18.0) 93 (13.5) 59 (8.6 36 (5.2) 23 (3.3)
Advertisements

Isha Changotra has wide experience in metals industry and is working for a renowned super alloys manufacturer located in China and United States. With extensive insight in metals and high performance super alloys, she aims to provide most useful information for folks engaged under this niche.

Tagged with: ,
Posted in Nimonic 80A alloy

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s

Metals, Alloys-Information Guide

Super metals and alloys

%d bloggers like this: